Conclusion
After analyzing the extruded copper samples, the following conclusions were obtained:
1) The stress generated by the cryogenic treatment of extruded copper resulted in vacancies,
dislocation redistribution, and new dislocations, which formed sub-grain boundaries.
This caused the
copper crystals to shrink and then grow within the test time range. The grain refinement effect
decreased at longer test times.
2) The copper crystals had different orientations in grains, the slip degree of each grain was
different, and the diffraction peak intensities of higher planes were also differe
....
4) During the cryogenic treatment, the hardness of each position of the sample was essentially
the same, and the effect of the cryogenic treatment on the grain refinement of the copper sample was
small. These two results are consistent with each othe
salut KIKI
cherchant des infos sur un lien possible entre la qualité du cuivre et l 'effet d'une cryogénisation, je suis tombé sur ceci
ou , d' après ce que je comprends , plus celui ci est pur , plus l'effet de la cryo à une influence
ici , sur la résistivité
![[Image: n362.png]](https://zupimages.net/up/23/52/n362.png)
je ne connaissais pas le terme RRR : https://en.wikipedia.org/wiki/Residual-resistance_ratio
d' après ce que j 'ai pu lire , un cuivre 3 N ( genre câble elec ,classique , cu 10.100 ) pourrait avoir un RRR d 'environ 500
un 8 N , un rapport RRR de plus de 10000 !
( jusqu’à 30000 !!! si des composés gazeux sont non présent )
quelque liens
( ma seine lecture du matin
)
https://www.copper.org/resources/properties/cryogenic/
https://patents.google.com/patent/WO2005073434A1/en
Citation :Des lors, est ce qu'on augmente alors la taille des cristaux ? Est ce qu"on reduit de façon durable la distance entre ces cristaux ? Ou completement autre chose ?
tiré du lien mis à dispo précédemment
https://iopscience.iop.org/article/10.10...033087/pdf
je cite ...
Conclusion
After analyzing the extruded copper samples, the following conclusions were obtained:
1) The stress generated by the cryogenic treatment of extruded copper resulted in vacancies,
dislocation redistribution, and new dislocations, which formed sub-grain boundaries.
This caused the
copper crystals to shrink and then grow within the test time range. The grain refinement effect
decreased at longer test times.
2) The copper crystals had different orientations in grains, the slip degree of each grain was
different, and the diffraction peak intensities of higher planes were also differe
....
4) During the cryogenic treatment, the hardness of each position of the sample was essentially
the same, and the effect of the cryogenic treatment on the grain refinement of the copper sample was
small. These two results are consistent with each othe
Citation :Effectivement , la conductivité intervient '!!. .. peut être faut il considérer après (et ou) l'indice de pureté N. : au mieux l'offre serait du CUIVRE Cu jusqu'a 8N ,
salut KIKI
cherchant des infos sur un lien possible entre la qualité du cuivre et l 'effet d'une cryogénisation, je suis tombé sur ceci
ou , d' après ce que je comprends , plus celui ci est pur , plus l'effet de la cryo à une influence
ici , sur la résistivité
![[Image: n362.png]](https://zupimages.net/viewer.php?id=23/52/n362.png)
je ne connaissais pas le terme RRR : https://en.wikipedia.org/wiki/Residual-resistance_ratio
d' après ce que j 'ai pu lire , un cuivre 3 N ( genre câble elec ,classique , cu 10.100 ) pourrait avoir un RRR d 'environ 500
un 8 N , un rapport RRR de plus de 10000 !
( jusqu’à 30000 !!! si des composés gazeux sont non présent )
quelque liens
( ma seine lecture du matin
)https://www.copper.org/resources/properties/cryogenic/
https://patents.google.com/patent/WO2005073434A1/en
my systeme "Phifi"
source ,Wadia 21 I ;Bi -amplification : Nakamichi Pa 7
enceintes Infinity Kappa 9a
Dcx 24/96 modifié
caissons Diy sur base 33 Focal associés à un Pioneer M90a
diffusion au plafond , hp diy ( Focal ) asservi par un Harman Kardon 7300 (mode logic 7 )
gestion des différents niveaux , pré MSB Technology
câble hp et secteur Diy
source ,Wadia 21 I ;Bi -amplification : Nakamichi Pa 7
enceintes Infinity Kappa 9a
Dcx 24/96 modifié
caissons Diy sur base 33 Focal associés à un Pioneer M90a
diffusion au plafond , hp diy ( Focal ) asservi par un Harman Kardon 7300 (mode logic 7 )
gestion des différents niveaux , pré MSB Technology
câble hp et secteur Diy